On the melting behavior of cyclic 1,4-butylene terephthalate for ring-opening polymerization and on polycondensation by enzymatic catalysis

Abstract

This thesis is divided into three parts. The first two parts deal with the ring-opening polymerization (ROP) of lactones, which is a viable route to polyesters. The high melting temperature of aromatic lactones like e.g. cyclic 1,4-butylene terephthalate (cBT) however limits their utilization, especially in reaction injection molding (RIM). The objective of the first two parts of this study was to evaluate possible ways of reducing this crucial parameter for an easier processing of cBT. In the third part, the polycondensation of a sustainable polyester by a metal- and an enzyme-catalyzed route were compared and evaluated.

Diese Dissertation ist in drei Teile gegliedert. Die ersten beiden Teile behandeln die ringöffnende Polymerisation (ROP) von Lactonen, was einen nützlichen Weg zu Polyestern darstellt. Die hohe Schmelztemperatur von aromatischen Lactonen, wie z.B. von cyclischem 1,4-Butylenterephthalat (cBT), begrenzt jedoch deren Anwendung. Das Ziel der ersten beiden Teile dieser Studie bestand in der Evaluierung von Wegen zur Reduktion dieses begrenzenden Faktors um eine einfachere Verarbeitung von cBT zu ermöglichen. Im dritten Teil wurde die Polykondensation eines nachhaltigen Polyesters per Katalyse mit Enzym sowie mit Metallkomplex verglichen und bewertet.