Titel: Investigation of magnetotransport properties in Ni/Pt and Co/Pd layered structures
Sonstige Titel: Untersuchung des Magnetotransports in Ni/Pt und Co/Pd Schichtsystemen
Sprache: Englisch
Autor*in: Farhadi Ghalati, Afsaneh
Erscheinungsdatum: 2018
Tag der mündlichen Prüfung: 2018-06-21
Zusammenfassung: 
In this thesis two topics in the field of magnetotransport properties of thin ferromagnetic layered structure in current in-plane (CIP) geometry are studied.
First the magnetoresistance effects in Ni/Pt system were investigated in the temperature range of 4.2 ≤ T ≤ 295 K. In Pt/Co/Pt the resistivity behaves as ρ(φ,θ) = ρt + Δρip cos2 φ sin2 θ + Δρop cos2 θ where φ/θ is the angle between magnetization and current direction/film normal. While Δρip is caused by the conventional AMR (bulk effect) a Δρop ∝ 1/t behavior was found for Pt(5nm)/Co(t)/Pt(3nm) sandwiches revealing that Δρop originates at the Co/Pt interfaces (anisotropic interface magnetoresistance (AIMR)). In order to study interfacial MR contribution in stacking isoelectronic materials Ni/Pt systems were investigated. We prepared Pt(5nm)/Ni(t)/Pt(3nm) sandwiches with Ni thicknesses of 1 – 50nm by DC magnetron sputtering on Si3N4 substrate. As a result, in contrast to previous findings, the ρ(θ) behavior can only be satisfactorily described when considering higher orders in the expansion of the MR: ρ(θ)=ρt + ∑n Δρ(op,2n) cos2n θ with n ≤ 3. The thickness dependence of the amplitudes Δρ(op,2n) behaves according to 1/t revealing that also the higher orders have their origin at the Ni/Pt interfaces.
The second topic of this thesis deals with investigation of the impact of aging on the various magnetoresistance effects in Pd/Co/Pd sandwiches at room temperature. By means of sputtering techniques two Pd(5 nm)/Co/Pd(3 nm) samples with 2 and 7nm Co thicknesses were fabricated on Si3N4 substrate and the longitudinal and transverse resistivity of the sandwiches were measured repeatedly over 600 days. The results show strong variations of the MR properties in the first three months followed by a slower change to equilibrium values. However, there are significant differences between both samples reflecting different behavior of Co/Pd systems governed by bulk-like or interface contributions. In order to find a correlation between the changes occurring in MR effects and the structural properties of the samples, XRR measurements accompanied the transport investigations over time. It is concluded that gradual intermixing of Co and Pd at the interfaces and absorption of hydrogen are the two mechanisms responsible for the aging effect in Pd/Co/Pd systems.
URL: https://ediss.sub.uni-hamburg.de/handle/ediss/7919
URN: urn:nbn:de:gbv:18-94075
Dokumenttyp: Dissertation
Betreuer*in: Oepen, Hans Peter (Prof. Dr.)
Enthalten in den Sammlungen:Elektronische Dissertationen und Habilitationen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat  
Dissertation.pdf7.93 MBAdobe PDFÖffnen/Anzeigen
Zur Langanzeige

Diese Publikation steht in elektronischer Form im Internet bereit und kann gelesen werden. Über den freien Zugang hinaus wurden durch die Urheberin / den Urheber keine weiteren Rechte eingeräumt. Nutzungshandlungen (wie zum Beispiel der Download, das Bearbeiten, das Weiterverbreiten) sind daher nur im Rahmen der gesetzlichen Erlaubnisse des Urheberrechtsgesetzes (UrhG) erlaubt. Dies gilt für die Publikation sowie für ihre einzelnen Bestandteile, soweit nichts Anderes ausgewiesen ist.

Info

Seitenansichten

20
Letzte Woche
Letzten Monat
geprüft am 14.04.2021

Download(s)

6
Letzte Woche
Letzten Monat
geprüft am 14.04.2021
Werkzeuge

Google ScholarTM

Prüfe